What are the disadvantages of quality after heat treatment of bearing parts?
| /*250*250 was created on 2017/12/25*/ var cpro_id = 'u3171089'; |
However, it is necessary to investigate the degree of overheating. It is necessary to investigate the microscopic arrangement. If the coarse needle-like martensite is present in the quenching arrangement of GCr15 steel, it is arranged for quenching and overheating. The cause of the quenching may be excessive heating or heating. The overheating caused by the too long time may also be due to the fact that the original arrangement of the banded carbide is severe; the low carbon zone between the two zones constitutes some martensite needle-like coarse; the composition is somewhat overheated. The retained austenite in the overheating arrangement Increase; scale stability is reduced. Because the quenching arrangement is overheated; the steel crystal is coarse; the resistance of the part is reduced; the impact resistance is reduced; the life of the bearing is also reduced. The overheating is severe and even constitutes a quenching crack.
If the under-heat quenching temperature is low or the cooling is poor, the tortite arrangement that exceeds the canonical rules will be attacked in the microscopic arrangement; it is called the underheating arrangement; it reduces the hardness; the wear resistance is drastically reduced; and the bearing life is affected.
Quenching cracked bearing parts are called quenching cracks due to internal stress during quenching and cooling. The causes of such cracks are: because the quenching heating temperature is too high or the cooling is too fast; the thermal stress and the metal mass volume change the arrangement stress It is greater than the fracture strength of the steel, the original defects of the work appearance (such as fine cracks or scratches on the surface) or the internal defects of the steel (such as slag inclusions, severe non-metallic inclusions, white spots, shrinkage holes, etc.) during quenching Constitutive stress gathering, severe surface decarburization and carbide segregation, lack of tempering after quenching of parts or tempering in time, the cold pressing stress of the previous process is too large, casting folding, deep turning tool marks, oil groove sharp edge The reason for the quenching crack may be one or more of the above factors; the existence of internal stress is the main reason for the quenching crack. The quenching crack is deep and slender; the fracture is straight; the fracture has no oxidation color. On the bearing ring, there are often longitudinal straight cracks or ring cracks. The shape of the bearing steel ball is S-shaped, T-shaped or ring-shaped. The quenching crack is characterized by two cracks. There is no decarburization appearance; significant difference and casting crack and data crack.
Heat treatment of deformed bearing parts during heat treatment; there are thermal stresses and arrangement stresses; such internal stresses can be superimposed or partially offset; they are complex and variable; because they can follow heating temperature, heating rate, cooling method, cooling rate, parts The shape and the size change; therefore, the heat treatment deformation is inevitable. Knowing and grasping the changing rules can make the deformation of the bearing parts (such as the ellipse of the ferrule, the scale increase, etc.) on a controllable scale; Of course. Mechanical bumps during heat treatment can also cause deformation of the parts; but this deformation can be reduced and prevented by improved operation.
The outer decarburization bearing parts are in the heat treatment process; if it is heated in an oxidizing medium; the surface will have an oxidation effect to reduce the mass fraction of the surface carbon of the part; the outer surface decarburization will be formed. The depth of the outer decarburization layer exceeds the final processing allowance. The part will be invalidated. The determination of the depth of the decarburization layer can be determined by the metallographic method and the microhardness method in the metallographic examination. The surface hardness measurement curve of the surface layer is the standard; the ruling criterion can be made.
The soft point is lack of heating; the cooling is poor; the quenching operation is not appropriate. The appearance of the bearing parts is somewhat hard. The appearance is called quenching soft point. It can form the same wear resistance and fatigue strength as the outer surface decarburization.
Recommend to friends comments close window
| Bearing related knowledge |
| FAFNIR, TORRINTON Bearings make up the equipment, application and protection knowledge of the coded automotive bearings Failure Analysis of SKF Bearings in the Medical Field Using Imported Bearings Analysis of the characteristics of the raceway noise of NSK bearings |
This article links to http://
Please indicate the bearing network http://
Previous:Analysis of the quality inspection method of bearing steel Next: How to remove the motor bearing from hot oil?
The Led Trunking System is divided into two parts, one is the trunking, the other is the functional component. At present, for trunking, we have 3 wires, 5 wires, 7 wires, 8 wires and 11 wires. The functional components include the emergency driver, Motion sensor module and track module.
The discription of all types of trunking.
3 Wire Trunking: N, L, E. (Basic Lighting)
5 Wire Trunking:
(1)L1, L2, L3, N, E (Basic Lighting)
(2)L,N,E, (Basic Lighting)+ Dimming
(3)L,N,E (Basic Lighting)+ Sensor
7 Wire Trunking:
(1)L,N,E (Basic Lighting)+ Sensor/Diming + Built-in Battery Emergency
(2)L1,L2,L3,N,E (Basic Lighting)+ Sensor/Diming
(3)L1,L2,N,E (Basic Lighting)+ Sensor/Diming+ Built-in Battery Emergency
8 Wire Trunking:
(1)L1,L2,L3,N,E (Basic Lighting)+ Sensor/Diming+ Built-in Battery Emergency
(2)L1,L2,N,E (Basic Lighting)+ Sensor+ Diming
(3)L,N,E (Basic Lighting)+ Sensor+ Diming+ Built-in Battery Emergency
11 Wire Trunking: (1)L1,L2,L3,N,E (Basic Lighting)+ Sensor/Diming+ 2xUPS Emergency
The function module:
Led Lights Trunking,Led Lighting Trunking,Led Trunking Lights,Dimmable Led Lights,Commercial Lighting Fixtures,Retail Lighting Design
SHENZHEN LITEHOME OPTOELECTRONIC TECHNOLOGY CO., LTD. , https://www.szlitehomelight.com